Please use this identifier to cite or link to this item: https://idr.l1.nitk.ac.in/jspui/handle/123456789/16236
Full metadata record
DC FieldValueLanguage
dc.contributor.authorKumar R.R.
dc.contributor.authorRaghvendra
dc.contributor.authorPandey S.K.
dc.contributor.authorPandey S.K.
dc.date.accessioned2021-05-05T10:30:00Z-
dc.date.available2021-05-05T10:30:00Z-
dc.date.issued2021
dc.identifier.citationSuperlattices and Microstructures Vol. 150 , , p. -en_US
dc.identifier.urihttps://doi.org/10.1016/j.spmi.2020.106787
dc.identifier.urihttp://idr.nitk.ac.in/jspui/handle/123456789/16236-
dc.description.abstract— This work reports the growth optimization and analysis of ZnO, MgxZn1-xO, and CdxZn1-xO thin films on silicon substrate using an electron beam evaporation system. The crystal phase purity, surface morphology, optical and electrical properties of deposited ZnO, MgxZn1-xO, and CdxZn1-xO thin films were studied. X-ray diffraction (XRD) spectra revealed that the deposited films were polycrystalline in nature with preferred (002) crystal orientation. Field emission scanning electron microscope study showed a dense-packed grained structure with an exact symmetrical distribution. The root-mean-square roughness of 3.03 nm was perceived by atomic force microscopy measurement for MgxZn1-xO thin-film, indicating good morphology of the deposited film. Photoluminescence measurement demonstrated a near-band-edge emission peak around 363 nm for ZnO thin film. The energy band gap obtained for ZnO, MgxZn1-xO, and CdxZn1-xO were 3.36 eV, 3.86 eV, and 2.89 eV, respectively, as measured by Ultraviolet–Visible spectroscopy. The higher amount of photocurrent was detected in illumination condition compared to dark condition with responsivity 0.54 AW-1 for ZnO films, making it suitable for photodiodes applications. © 2020 Elsevier Ltden_US
dc.titleExperimental investigation and comparative analysis of electron beam evaporated ZnO/MgxZn1-xO/CdxZn1-xO thin films for photodiode applicationsen_US
dc.typeArticleen_US
Appears in Collections:1. Journal Articles

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.